| Abstract [eng] |
Biomass is one of the most important sources of renewable energy, generating large amounts of ash. This increases the amount of waste, landfill, and air pollution. This work focuses on the sustainable disposal of this ash by producing an innovative binder. The mechanical and microstructural properties of alkali-activated biomass fly ash (BFA) and diatomite (DT) mixtures are currently insufficiently studied. New scientific knowledge of these properties is needed. This study presents the possibility of using BFA and diatomite as aluminosilicate precursors for the production of an alkaline-activated binder. It was found that the reactivity of BFA is relatively low. Based on XRD analysis, the mineral composition of BFA is dominated by quartz and calcite, both of which are non-reactive minerals. Therefore, mixtures with DT were created as precursors. According to Rietveld analysis data, an amorphous part was found in both precursor materials, BFA and DT. Comparing the chemical composition of BFA and DT using XRF and Rietveld analysis data, it was found that the amorphous part of BFA consists of CaO, while the amorphous part of DT consists of SiO2. Thus, the combination of these precursors should complement each other during the geopolymerisation process. After 28 days of curing, the strength of the binders was dependent on the amount of DT, and the highest strength values, such as 16.4 MPa and 15.3 MPa, were obtained when DT contents were 10% and 30%, respectively. After geopolymerisation, XRD analysis showed that calcium silicate hydrate, hydrotalcite, and calcium aluminium silicate hydrate (zeolite A type) were formed. SEM analysis confirmed the XRD results and showed that DT additives (10% and 30% by weight) improved the microstructure of alkali-activated BFA, which is closely related to compressive strength values. The proposed binder will be useful in the preparation of concrete, which could be used for artificial aggregates or small architectural elements. |